Erosion resistance of slip cast composite Al2O3- ZrO2 ceramics (CROSBI ID 619227)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Majić Renjo, Marijana, Ćurković, Lidija, Grilec, Krešimir
engleski
Erosion resistance of slip cast composite Al2O3- ZrO2 ceramics
In this paper, erosion resistance of slip cast monolithic (Al2O3) and composite (Al2O3–t-ZrO2) ceramics was investigated by dry silica sand (SiO2) erodent. The amount of t-ZrO2 in powder mixture of Al2O3–t-ZrO2 was 5 wt. % and 10 wt. %. The erosive wear behaviour was studied at following impact angles of erodent: 30°, 60° and 90°. Erosion mechanisms of all prepared ceramic samples were evaluated by measuring the roughness parameters (Ra, Rz, Rmax) and weight loss, as well as analysis of surface morphology by means of scanning electron microscope (SEM). Obtained results showed that tribological properties of monolithic Al2O3 can be improved with the addition of t-ZrO2. It was also found that erosion resistance increases with the increasing amount of t-ZrO2 in the powder mixture. Generally, for all investigated ceramic samples erosion resistance decreases by the increasing erodent impact angle.
alumina (Al2O3); zirconia (ZrO2); Al2O3–ZrO2 composite ceramics; erosion resistance; slip casting
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
2014.
objavljeno
Podaci o matičnoj publikaciji
The 25th DAAAM International Symposium Intelligent Manufacturing & Automation
Podaci o skupu
The 25th DAAAM International Symposium Intelligent Manufacturing & Automation
predavanje
26.11.2014-29.11.2014
Beč, Austrija