Karakterizacija elektrodeponiranih rutenijevih elektroda metodom impedancijske spektroskopije (CROSBI ID 481708)
Prilog sa skupa u zborniku | izvorni znanstveni rad | domaća recenzija
Podaci o odgovornosti
Horvat-Radošević, Višnja ; Kvastek, Krešimir
njemački
Karakterizacija elektrodeponiranih rutenijevih elektroda metodom impedancijske spektroskopije
The interfacial region of electrodeposited ruthenium and 0.5 mol dm-3 H2SO4 had been studied by use of the impedance spectroscopy over potentials between -0.30 V and +0.65 V vs. SCE. Three well defined potential domains with characteristic impedance/frequency responses were observed, with the two-step hydrogen evolution reaction dominant between -0.30 V and -0.05 V, fast oxidation of "active" ruthenium atoms and consequent adsorpetion pf oxygen containing species (H2O or OH-) dominant between 0.00 V and +0.45 V, and the regular oxide film formation after +0.45 V vs. SCE.
nije evidentirano
nije evidentirano
engleski
Characterization of electrodeposited ruthenium electrodes by impedance spectroscopy
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
85-88-x.
2001.
objavljeno
Podaci o matičnoj publikaciji
2.Hrvatski simpozij o elektrokemiji, Zbornik radova, Primošten, 17.-20. rujna 2001.
Gojo, M
Zagreb: Hrvatsko društvo kemijskih inženjera i tehnologa (HDKI)
Podaci o skupu
2.Hrvatski simpozij o elektrokemiji
predavanje
17.09.2001-20.09.2001
Primošten, Hrvatska