SEM-EDS analysis of slip cast composite Al2O3-ZrO2 ceramics (CROSBI ID 614497)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Majić Renjo, Marijana ; Ćurković, Lidija ; Grilec, Krešimir ; Sakoman, Matija ; Jakovljević, Suzana
engleski
SEM-EDS analysis of slip cast composite Al2O3-ZrO2 ceramics
In this paper, composite Al2O3–t-ZrO2 ceramics (composition: 95 wt. % Al2O3 – 5 wt. % t-ZrO2 and 90 wt. % Al2O3 – 10 wt. % t-ZrO2) was formed by slip casting in plaster mould. After drying, green bodies were sintered in laboratory electric kiln under air environment at a temperature of 1650 °C. Density of prepared samples was determined by the Archimedes' method. Surface morphology of sintered composite ceramics samples was determined by scanning electron microscope (SEM) equipped with energy dispersive spectrometer (EDS) analysis. Distribution of the elements aluminium (Al), zirconium (Zr) and oxygen (O) on fracture surfaces of sintered samples was determined by EDS mapping. SEM-EDS analysis of prepared composite ceramics samples confirmed the homogeneous distribution of ZrO2 in Al2O3 matrix.
Slip casting; Al2O3–t-ZrO2 ceramics; SEM-EDS
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
95-98.
2014.
objavljeno
Podaci o matičnoj publikaciji
Živković, Dražen
Split: Hrvatsko društvo za zaštitu materijala (HDZaMa)
1847-7917
Podaci o skupu
4th international conference Mechanical technologies and structural materials
predavanje
25.09.2014-26.09.2014
Split, Hrvatska