Evaluation of surface roughness of slip cast composite Al2O3-ZrO2 ceramics in solid particle erosion (CROSBI ID 613927)
Prilog sa skupa u zborniku | sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Grilec, Krešimir ; Majić Renjo, Marijana ; Ćurković, Lidija ; Sakoman, Matija ; Baršić, Gorana
engleski
Evaluation of surface roughness of slip cast composite Al2O3-ZrO2 ceramics in solid particle erosion
In this paper, surface roughness parameters (Ra, Rmax, Rz) of monolithic and composite ceramics produced by slip casting were monitored before and after solid particle erosion. Prepared samples were monolithic Al2O3 and composite Al2O3–t-ZrO2 ceramics (composition: 95 wt. % Al2O3 – 5 wt. % t-ZrO2 and 90 wt. % Al2O3 – 10 wt. % t-ZrO2). The erosive wear behaviour was studied at the impact angle of 90°, using dry silica sand (SiO2) as an erodent. Obtained results indicated that values of roughness parameters increased after erosion, and the largest increase was observed for monolithic Al2O3 ceramics. Surface roughness parameter values decrease with the increase of ZrO2 content. Obtained results showed that tribological properties of monolithic Al2O3 can be improved with the addition of t-ZrO2.
Al2O3 ; Al2O3–t-ZrO2 ceramics ; solid particle erosion
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
79-79.
2014.
objavljeno
Podaci o matičnoj publikaciji
Podaci o skupu
Sixteenth Annual conference YUCOMAT 2014
poster
01.09.2014-05.09.2014
Herceg Novi, Crna Gora