Erosion resistance of sol-gel TiO2-ZrO2 film on stainless steel
Wear resistance of metallic materials can be improved by modifying their surface with different coating deposition techniques, one of which is a sol-gel technology. In this paper, the erosive wear resistance of a ceramic nanostructured sol-gel TiO2-ZrO2 film deposited on the stainless steel substrate (X5CrNi18-10) by the dip coating technique has been described. Dry silica sand was used as erodent, with impact angle of 30 and 90. The coating thickness, as well as chemical composition after erosion, was analyzed by the Glow Discharge Optical Emission Spectrometer (GD- OES). Wear scars were analyzed by the scanning electron microscope (SEM). Obtained results showed that erosive wear resistance of the sol- gel TiO2-ZrO2 film significantly depends on the erodent impact angle, while the erosive wear resistance decreases with the impact angle increase.
sol-gel TiO2-ZrO2 film ; wear resistance
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
99-99.
2014.
objavljeno
Podaci o matičnoj publikaciji
YUCOMAT 2014
Stojičić, Aleksandra
Herceg Novi:
Podaci o skupu
Sixteenth Annual conference YUCOMAT 2014
poster
01.09.2014-05.09.2014
Herceg Novi, Crna Gora