Erosion mechanisms of slip cast composite Al2O3-ZrO2 ceramics (CROSBI ID 612384)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Sakoman, Matija ; Grilec, Krešimir ; Ćurković, Lidija ; Majić Renjo, Marijana ; Sladojević, Milan
engleski
Erosion mechanisms of slip cast composite Al2O3-ZrO2 ceramics
In this paper highly concentrated (70 wt. %) aqueous Al2O3 and Al2O3–t-ZrO2 suspensions were prepared. Dispersant DOLAPIX CE64 was used for stabilization. Green bodies were formed by slip casting process in plaster mould. After drying, green bodies were sintered at a temperature of 1650 °C. SEM-EDS analysis of prepared samples confirmed the homogeneous distribution of ZrO2 in Al2O3 matrix. Erosive wear resistance of sintered monolithic Al2O3 and composite Al2O3–t-ZrO2 ceramics was determined by SEM analysis of the sample surface morphology before and after erosion at impact angle of 90° and SiO2 as erodent particles. Surface morphology analysis after erosion showed that wear scars were significantly larger on Al2O3 than on Al2O3–t-ZrO2 samples. All conducted tests showed that tribological properties of monolithic Al2O3 can be improved with the addition of t-ZrO2.
Al2O3; Al2O3-t-ZrO2; slip casting; solid particle erosion
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
503-508.
2014.
objavljeno
Podaci o matičnoj publikaciji
MATRIB 2014
Šolić, Sanja ; Šnajdar Musa, Mateja
Zagreb: Hrvatsko društvo za materijale i tribologiju (HDMT)
1848-5340
Podaci o skupu
International conference MATRIB 2014 "Materials, tribology, recycling"
predavanje
26.06.2014-28.06.2014
Korčula, Hrvatska; Vela Luka, Hrvatska