IMPROVEMENT OF CORROSION RESISTANCE OF THE STAINLESS STEEL BY SOL-GEL TiO2–ZrO2 FILMS (CROSBI ID 608970)
Prilog sa skupa u zborniku | sažetak izlaganja sa skupa | domaća recenzija
Podaci o odgovornosti
Bačić, Ivana ; Ćurković, Lidija ; Otmačić Ćurković, Helena ; Vugrinčić, Amalija ; Levačić, Lidija
engleski
IMPROVEMENT OF CORROSION RESISTANCE OF THE STAINLESS STEEL BY SOL-GEL TiO2–ZrO2 FILMS
Single layer thin films of TiO2–ZrO2 were deposited on the AISI 316L austenitic stainless steel by sol-gel process and dip coating method to improve its corrosion resistance properties. For the preparation of sol titanium isopropoxide and zirconium butoxide were used as precursors, i- propanol as a solvent with addition of nitric acid as a catalyst, acetylacetone as a chelating agent and water for hydrolysis. Deposited films were calcined at the temperature of 400 °C and 600 °C. Thickness of sol-gel TiO2– ZrO2 films deposited on stainless steel was determined by glow-discharge optical emission spectrometry (GD-OES). The morphology of the film was analysed by SEM-EDS. The corrosion behavior of stainless steel, coated by amorphous films, was evaluated in 3.5 wt.% NaCl by potentiodynamic polarization and electrochemical impedance spectroscopy techniques. It was found that the sol-gel TiO2–ZrO2 films with amorphous structure and deposited by the sol–gel process enhance the corrosion properties of AISI 316L in chloride media.
sol-gel film; corrosion; stainless steel
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
201-201.
2014.
objavljeno
Podaci o matičnoj publikaciji
X. Susret mladiih kemijskih inženjera, KNJIGA SAŽETAKA, Book of abstracts
Findrik Blažević, Z. ; Sudar M. ; Šalić A. ; Vrasalović Presečki A. ; Vrsaljko D.
Zagreb:
987-953-6470-65-5
Podaci o skupu
X. Susret mladiih kemijskih inženjera
poster
20.02.2014-21.02.2014
Zagreb, Hrvatska