Influence of heat treatment on properties of ti-nb alloys


Kunčicka, L.; Štěpan, P.; Kliber, J.; Mamuzić, Ilija
Influence of heat treatment on properties of ti-nb alloys // Metalurgija, 53 (2014), 2; 186-188 (međunarodna recenzija, članak, znanstveni)


Naslov
Influence of heat treatment on properties of ti-nb alloys

Autori
Kunčicka, L. ; Štěpan, P. ; Kliber, J. ; Mamuzić, Ilija

Izvornik
Metalurgija (0543-5846) 53 (2014), 2; 186-188

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Titanium; oxygen content; microhardness

Sažetak
Ti-Nb alloys are of a large potential for industrial, as well as biomedical utilisation. Oxygen content in the alloy is a parameter influencing its properties and cannot be neglected. The main focus of this paper is on observation of influence of annealing time on oxygen content in the structure of Ti – 20, 7 (at.)% Nb alloy. Four groups of the samples were annealed at the temperature of 800 °C from 15 to 60 minutes with 15 min. step. As it was proven by the analysis, the oxygen content increased with increasing annealing time. Moreover, microhardness measurements showed increasing trend of HV microhardness value with increasing oxygen content.

Izvorni jezik
Engleski

Znanstvena područja
Metalurgija



POVEZANOST RADA


Projekt / tema
120-1201787-1491 - Oblikovanje deformiranjem i svojstva novih metalnih materijala (Ilija Mamuzić, )

Ustanove
Fakultet strojarstva i brodogradnje, Zagreb

Autor s matičnim brojem:
Ilija Mamuzić, (27862)

Časopis indeksira:


  • Web of Science Core Collection (WoSCC)
    • Science Citation Index Expanded (SCI-EXP)
    • SCI-EXP, SSCI i/ili A&HCI
  • Scopus


Uključenost u ostale bibliografske baze podataka:


  • METADEX: Metals Science
  • Metals Absctracts
  • EI Compendex Plus
  • PaperChem, Metadex
  • Chemical Abstracts
  • Mechanical Engineering Abstracts
  • Aluminium Industry Abstracts
  • Dialog Sourceone (SM) Engineering
  • Energy Science Technology
  • Engineered Materials Abstracts
  • Analitical Abstracts Online
  • Embase
  • Scopus...