Hydration of B2O3-stabilized α′- and β-modifications of dicalcium silicate (CROSBI ID 192316)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Jelenić, Ivanka ; Bezjak, Aleksandar ; Bujan, Marija
engleski
Hydration of B2O3-stabilized α′- and β-modifications of dicalcium silicate
Paste hydration of B2O3-stabilized α′- and β-C2S was studied at reaction times between 5 hours and 28 days. Data on the degree of hydration determined by X-ray diffraction at different ages were used to evaluate hydration rate constants. The higher rate of α′- C2S hydration resulted in the higher compressive strengths of the α′-C2S-alite paste as compared with the β-C2S-alite paste. Differences in crystal imperfections of the two C2S-polymorphs were determined using electron microscopy and electron diffraction
cement ; hydration ; dicalcium silicate
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
8 (2)
1978.
173-180
objavljeno
0008-8846
1873-3948
10.1016/0008-8846(78)90006-6