Susceptibility to corrosion of welded AlMgSi alloy EN AW 6060 (CROSBI ID 587380)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Radošević, Jagoda ; Malina, Jadranka ; Dolić, Natalija ; Ljumović, Petar ; Slavica - Matešić, Sanja
engleski
Susceptibility to corrosion of welded AlMgSi alloy EN AW 6060
Electrochemical tests on welded joints of commercial extruded Al-alloy EN AW-6060 were carried out in this article to assess corrosion behavior in a solution with 3.5% NaCl content. Potentiodynamic techniques such as Tafel Polarization and Cyclic Anodic Polarization were used to observe resistance to general corrosion and the tendency of piting to appear. The results showed that the disturbance zone has a cathodic character in comparison to the base leg so that the current passivity is higher while the piting potential Epit and the Erp lowering potential are smaller for samples made from welded AlMgSi tile.
Corrosion of welded AlMgSi alloy EN AW-6060 ; Chloride medium
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
97-104.
2012.
objavljeno
Podaci o matičnoj publikaciji
Drugi međunarodni simpozijum o koroziji i zaštiti materijala i životnoj sredini : knjiga radova
Vuksanović, Darko ; Zejnilović, Refik ; Pješčić, Jelena ; Bošković, Ivana ; Radovnjić, Dragan
Bar: Crnogorsko društvo za koroziju, zaštitu materijala i životne sredine
978-9940-9334-1-8
Podaci o skupu
Međunarodni simpozijum o koroziji i zaštiti materijala i životnoj sredini
predavanje
17.10.2012-20.10.2012
Bar, Crna Gora