Primjena niskotemperaturnog aluminiziranja kod čelika za topli rad (CROSBI ID 586590)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Matijević ; Božidar
hrvatski
Primjena niskotemperaturnog aluminiziranja kod čelika za topli rad
During die-casting of aluminium components, tool parts are exposed to a complex combination of different wear mechanisms, such as thermal fatigue, erosion and reactive soldering of the die surfaces. As a result, this causes damage and severely reduces the durability of tools, thus increasing tools maintenance costs. For increased resistance to reaction soldering, different methods of thermo-chemical surface modification techniques (such as nitriding or vanadising) or different processes of coatings may be applied. In this paper, the possibility of using low-temperature, low-potential aluminizing with subsequent oxidation of aluminized hot work tool steel surface has been explored. In this case, formation of stable and compact aluminium oixide (Al2O3) layer is what prevents direct contact of molten metal with the base die alloy, making it resistant (to some extent) to reaction soldering.
aluminiziranje; reaktivno nataljenje; erosija; tlačni lijev
nije evidentirano
engleski
Application of low temperature aluminizing on hot work tool steels
nije evidentirano
aluminising; reactive soldering; erosion; die casting
nije evidentirano
Podaci o prilogu
51-56.
2012.
objavljeno
Podaci o matičnoj publikaciji
International conference Heat treatment and surface engineering - European opportunities for Croatian economy : proceedings book = Međunarodno savjetovanje Toplinska obrada i inženjerstvo površina - europske mogućnosti hrvatskog gospodarstva : zbornik radova
Smoljan, Božo ; Iljkić, Dario
Rijeka: Hrvatsko društvo za toplinsku obradu i inženjerstvo površina
978-953-7690-03-8
Podaci o skupu
Međunarodno savjetovanje Toplinska obrada i inženjerstvo površina - europske mogućnosti hrvatskog gospodarstva
predavanje
11.05.2012-11.05.2012
Rijeka, Hrvatska