Modificiranje površina dijelova kalupa za tlačno lijevanje aluminija
Mould parts for aluminium die casting are exposed to a complex wear mechanism and therefore their life is limited. A predominant wear mechanism is the reaction-melting of the mould part working surface, which results in frequent outages and increased mould maintenance costs. In order to extend the life of moulds for aluminium die casting, different procedures of modification and surface coating are applied. So far, the most commonly used procedure has been the salt bath nitriding (the TENIFER process), but data from literature point to the efficient application of diffusion carbide coating, particularly to vanadising due to high chemical and tribological resistance of vanadium carbide.
tlačni lijev; trošenje; test uranjanja; nitriranje; vanadiranjE
nije evidentirano
engleski
Surface modification of aluminium die casting die
nije evidentirano
die casting; tribology; imersion test; nitriding; vanadizing
nije evidentirano
Podaci o prilogu
131-142.
2006.
objavljeno
Podaci o matičnoj publikaciji
Grilec, Krešimir
Zagreb: Hrvatsko društvo za materijale i tribologiju (HDMT)
953-7040-10-0
Podaci o skupu
International conference on Materials tribology processing
predavanje
22.06.2006-24.06.2006
Vela Luka, Hrvatska