Abrasion resistance of DLC coatings (CROSBI ID 476892)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Grilec, Krešimir ; Schauperl, Zdravko ; Prusac, Denis ; Oršanić, Želimir
engleski
Abrasion resistance of DLC coatings
Tribological use of DLC (diamond-like carbon) coatings nowadays includes sliding components and cutting tools for non-ferrous alloys, such as aluminum, copper, magnesium and lead alloys, and non-metals, such as fibre-reinforced polymers and other composites, semi-sintered ceramics, cold-pressed cemented carbides, graphite, silicon, hard rubbers and wood. Since materials of higher hardness as a rule have higher abrasion resistance, it is reasonably to expect an increase of abrasion resistance when materials are coated by DLC . Abrasion resistance of a DLC coating was examined in this work. The substrate of a tool steel was hardened and tempered to a range of hardness and then coated by plasma activated chemical vapour deposition (PACVD). Abrasion wear testing was done according to a modified ASTM G 65-94 procedure.
tribology; DLC coatings; abrasion resistance
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
IV065-IV072.
1999.
objavljeno
Podaci o matičnoj publikaciji
Proceedings of the 5th International Scientific Conference on Production Engineering CIM'99 - Computer Integrated Manufacturing and High Speed Machining
Cebalo, Roko ; Schulz, Herbert
Zagreb: Hrvatska udruga proizvodnog strojarstva (HUPS)
953-97181-1-2
Podaci o skupu
International Scientific Conference on Production Engineering (5 ; 1999)
predavanje
17.06.1999-18.06.1999
Opatija, Hrvatska