The influence of heat treatment by annealing on clad plates residual stresses


Mateša, Branko; Kozak, Dražan; Stoić, Antun; Samardžić, Ivan
The influence of heat treatment by annealing on clad plates residual stresses // Metalurgija, 50 (2011), 4; 227-230 (podatak o recenziji nije dostupan, izvorni znanstveni rad, znanstveni)


Naslov
The influence of heat treatment by annealing on clad plates residual stresses

Autori
Mateša, Branko ; Kozak, Dražan ; Stoić, Antun ; Samardžić, Ivan

Izvornik
Metalurgija (0543-5846) 50 (2011), 4; 227-230

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, izvorni znanstveni rad, znanstveni

Ključne riječi
Residual stresses; heat treated clad plates; centre-blind holes drilling; electrical resistance strain gauges (rosettes)

Sažetak
The influence of applied clad procedure as well as heat treatment by annealing (650 °C/2h) on level and nature of residual stresses was researched. Three clad procedure are used i.e. hot rolling, submerged arc welding (SAW) with strip electrode and explosion welding. The relaxed deformation measurement on clad plate surfaces was performed by applying centre-hole drilling method using special measuring electrical resistance strain gauges (rosettes). After performed measuring, size and nature of residual stresses were determined using analytical method. depending of residual stresses on depth of drilled blind-hole is studied.

Izvorni jezik
Engleski

Znanstvena područja
Strojarstvo



POVEZANOST RADA


Projekt / tema
152-0000000-3309 - Suvremene tehnike obrade rezanjem u proizvodnji prihvatljivoj okolišu (Antun Stoić, )
152-1201910-1909 - Analiza i procjena loma konstrukcija iz anizotropnih materijala (Dražan Kozak, )
152-1521473-1476 - Suvremene tehnologije spajanja lakih strojarskih konstrukcija (Ivan Samardžić, )

Ustanove
Strojarski fakultet, Slavonski Brod

Časopis indeksira:


  • Web of Science Core Collection (WoSCC)
    • Science Citation Index Expanded (SCI-EXP)
    • SCI-EXP, SSCI i/ili A&HCI
  • Scopus