The study of coal tar epoxy protective coatings by impedance spectroscopy


Babić, Ranko; Metikoš-Huković, Mirjana; Radovčić, Hedviga
The study of coal tar epoxy protective coatings by impedance spectroscopy // Progress in organic coatings, 23 (1994), 3; 275-286 doi:10.1016/0033-0655(94)80004-9 (međunarodna recenzija, članak, znanstveni)


Naslov
The study of coal tar epoxy protective coatings by impedance spectroscopy

Autori
Babić, Ranko ; Metikoš-Huković, Mirjana ; Radovčić, Hedviga

Izvornik
Progress in organic coatings (0300-9440) 23 (1994), 3; 275-286

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Steel panels; coal tar epoxy; impedance spectroscopy

Sažetak
Steel panels coated with a coal tar epoxy composition were studied by impedance spectroscopy in the dry condition as well as during exposure to synthetic seawater and to 10% NaOH solution. In the temperature range from 0 to 20 °C the dry coating behaves as an almost ideal capacitor with a dielectric constant ranging from 3.0 to 3.2. The coal tar epoxy coating immersed in synthetic seawater showed capacitative behaviour over a long period of exposure, in the frequency range 100 Hz to 100 kHz. However, the thinner coatings (~50 μm) were subject to a permanent slow degradation and their resistance decreased to approximately 107 Ωcm2 after 7 months of continuous immersion, whereas the degradation process for thicker coatings (~125 μm) was slower and the resistance was still above 108 Ωcm2 after 9 months of continuous immersion. The water uptake showed an initial rapid rise to between 9 and 13%. The coating degradation in a 10% NaOH solution is rather more rapid and after only one day of immersion a coating resistance of 106 Ωcm2 and a water uptake of 30% was found.

Izvorni jezik
Engleski

Znanstvena područja
Kemija



POVEZANOST RADA


Ustanove
Fakultet kemijskog inženjerstva i tehnologije, Zagreb

Časopis indeksira:


  • Current Contents Connect (CCC)
  • Web of Science Core Collection (WoSCC)
    • SCI-EXP, SSCI i/ili A&HCI
  • Scopus


Citati