FLEXURAL STRENGTH OF ALUMINA CERAMICS: WEIBULL ANALYSIS


Ćurković, Lidija; Bakić, Ante; Kodvanj, Janoš; Haramina, Tatjana
FLEXURAL STRENGTH OF ALUMINA CERAMICS: WEIBULL ANALYSIS // Transactions of FAMENA, 34 (2010), 1; 13-19 (međunarodna recenzija, članak, znanstveni)


Naslov
FLEXURAL STRENGTH OF ALUMINA CERAMICS: WEIBULL ANALYSIS

Autori
Ćurković, Lidija ; Bakić, Ante ; Kodvanj, Janoš ; Haramina, Tatjana

Izvornik
Transactions of FAMENA (1333-1124) 34 (2010), 1; 13-19

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Flexural strength; alumina ceramics; Weibull distribution

Sažetak
In this paper, flexural strength, fs, of cold isostatically pressed (CIP) high purity alumina ceramics was determined by the three-point bend test. It was found that flexural strength shows a large variation and can be described by a two-parameter Weibull distribution function, with the scale parameter 0, and the Weibull modulus m. These parameters were determined by the linear regression using the measured values of fs. It was found that the measured flexural strength, fs, of alumina ceramics follows the Weibull distribution. The flexural strength values were found to range from 266.7 to 357.5 MPa.

Izvorni jezik
Engleski

Znanstvena područja
Strojarstvo



POVEZANOST RADA


Projekt / tema
120-1201833-1789 - Istraživanje strukture i svojstava tehničke keramike i keramičkih prevlaka (Lidija Ćurković, )
120-1201910-1907 - Eksperimentalna simulacija oštećenja mehaničkih i biomehaničkih sustava (Janoš Kodvanj, )

Ustanove
Fakultet strojarstva i brodogradnje, Zagreb

Časopis indeksira:


  • Web of Science Core Collection (WoSCC)
    • Science Citation Index Expanded (SCI-EXP)
    • SCI-EXP, SSCI i/ili A&HCI
  • Scopus


Uključenost u ostale bibliografske baze podataka:


  • Science Citation Index Expanded
  • Journal of Citation Reports/Science Edition
  • GEOBASE
  • Water Resources Abstracts
  • CSA Engineering Research Database
  • Scopus