Damage Level Estimate of API J55 Steel for Welded Seam Casing Pipes (CROSBI ID 156893)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Šarkoćević, Živče ; Arsić, Miodrag ; Međo, Bojan ; Kozak, Dražan ; Rakin, Marko ; Burzić, Zijah ; Sedmak, Aleksandar
engleski
Damage Level Estimate of API J55 Steel for Welded Seam Casing Pipes
The subject of this paper is investigation of the damage level of API J55 steel, used for manufacturing the casing pipes by high frequency (HF) contact welding. The analysed pipe was withdrawn after about 70 000 hours of service in an oil drilling rig. Experimental analysis included determining the mechanical properties of the base material and welded joint, in particular the tensile and impact toughness testing. Fracture behaviour is examined by testing the modified compact tension (CT) specimens machined with a pre-crack in the base metal, weld metal and heat affected zone (HAZ). The critical value of the stress intensity factor KIc is determined using the critical value of the J integral JIc, because the plane strain conditions for fracture toughness could not be satisfied. Fatigue crack growth rate and fatigue threshold stress intensity factor range are determined by three point bending tests of the Charpy specimens with a V-notch in each of the three zones of the welded joint. The investigation conducted on specimens cut from the exploited pipe and the new pipe of the same grade revealed that the material properties were not seriously deteriorated during the analyzed period of service.
Casing pipe; Damage level; High frequency contact welding; Pipe integrity
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano