WEIBULL ANALYSIS OF FLEXURAL STRENGTH OF COLD ISOSTATICALLY PRESSED ALUMINA CERAMICS (CROSBI ID 553196)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Ćurković, Lidija ; Kodvanj, Janoš ; Bakić, Ante ; Haramina, Tatjana
engleski
WEIBULL ANALYSIS OF FLEXURAL STRENGTH OF COLD ISOSTATICALLY PRESSED ALUMINA CERAMICS
Flexural strength,  fs, of cold isostatically pressed alumina ceramics, (CIP)-Al2O3, with a purity of 99.8 % was determined by the three - point bend test. The flexural strength was found to range from 266.7 to 372.2 MPa. It is well known that the measured fracture of brittle ceramics shows large variability. Therefore, the probabilistic characteristics of the flexural strength were analysed by a two-parameter Weibull distribution function, with a scale parameter,  0, and the Weibull modulus, m. These parameters were determined by the linear regression method for  fs data measured. It was found that the measured flexural strength,  fs, of alumina ceramics follows the Weibull distribution.
flexural strength; alumina ceramics; Weibull distribution
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
49-55.
2009.
objavljeno
Podaci o matičnoj publikaciji
MATRIB 2009 ; Materials, tribology, processing
Grilec, Krešimir ; Mrić, Gojko
Zagreb: Hrvatsko društvo za materijale i tribologiju (HDMT)
978-953-7040-16-1
Podaci o skupu
Materials, tribology, processing
poster
24.06.2009-26.06.2009
Vela Luka, Hrvatska