Characterisation of ZrO2 layers deposited on Al2O3 coating (CROSBI ID 535945)
Prilog sa skupa u zborniku | ostalo | međunarodna recenzija
Podaci o odgovornosti
Jakovljević, Suzana ; Hendrix, Willy ; Havermans, Danny ; Meneve, Jan
engleski
Characterisation of ZrO2 layers deposited on Al2O3 coating
The paper describes a method of coating which combines two different methods of producing the layers. The first layer is Al2O3 produced by plasma spraying with thickness of around 200  m which was deposited on the stainless steel (EN X22CrMoV121) substrate. After that, ZrO2 layer was deposited on the Al2O3 coating by a sol-gel process using dip coating technique. The dip coating process was performed four and eight times respectively in order to see the influence of number of layers and annealed at three different temperature (400º ; C, 700º ; C and 1000º ; C). In experimental work, coating produced by this method were tested on micro-scale abrasion, scratch testing and ball on disc test. The result shows that sol-gel ZrO2 layers decrease coefficient of friction and wear factor determined by ball on disc test.
Sol-gel; Plasma spraying; Coefficient of friction
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
625-637.
2007.
objavljeno
Podaci o matičnoj publikaciji
ECOTRIB 2007 Joint European Conferance on Tribology and Final conferance of COST 532 action
Vižentin, Jože ; Podgornik, Bojan ; Holmberg, Kenneth ; Ciulli Enrico ; Franek, Friedrich
Ljubljana: Slovenian Society for Tribology
978-961-90254-8-2
Podaci o skupu
ECOTRIB 2007 Joint European Conferance on Tribology and Final conferance of COST 532 action
predavanje
12.06.2007-15.06.2007
Ljubljana, Slovenija