Crystallization of amorphous Al2O3– SiO2 precursors doped with nickel (CROSBI ID 133355)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Tkalčec, Emilija ; Kurajica, Stanislav ; Schmauch, Joerg Crystallization of amorphous Al2O3– SiO2 precursors doped with nickel // Journal of non-crystalline solids, 353 (2007), 30-31; 2837-2844-x

Podaci o odgovornosti

Tkalčec, Emilija ; Kurajica, Stanislav ; Schmauch, Joerg

engleski

Crystallization of amorphous Al2O3– SiO2 precursors doped with nickel

The crystallization of amorphous diphasic Al2O3-SiO2 precursors doped with nickel has been studied by differential scanning calorimetry (DSC), XRD diffraction (XRD) and scanning and transmission electron microscopy (SEM, TEM) equipped with energy dispersive X-ray spectroscopy (EDS). Diphasic gels with constant atomic ratio (Al + Ni)/Si = 3:1, where 0, 1, 2 and 3 at.% of aluminum were replaced by nickel, have been prepared by hydrolyzing of TEOS in aqueous solution of aluminum nitrate. Crystallization of Ni-containing gamma-Al2O3 preceded the crystallization of Al-Si spinel. Activation energy of 603 ± ; ; ; 16 kJ mol-1 for crystallization of Ni-containing gamma- Al2O3 was obtained in non-isothermal conditions. Ni-incorporated gamma-Al2O3 transforms gradually with the temperature increase into Ni aluminate spinel, while Al-Si spinel reacts with amorphous silica forming mullite at about 1200 oC. Rietveld structure refinement of phases present in the samples annealed at 1600 oC and SEM-EDS and TEM-EDS analyses of related phases have shown that nickel predominantly crystallizes as NiAl2O4, but small amount of nickel is incorporated in mullite structure, as well as, dissolved in the glassy phase of the system.

Ni-aluminate spinel; mullite; sol-gel; crystallization; XRD; SEM; TEM

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

353 (30-31)

2007.

2837-2844-x

objavljeno

0022-3093