PERFORMANCE OF LOW-SILICON VACUUM REMELTED HOT WORK TOOL STEEL UNDER HIGH THERMAL LOAD (CROSBI ID 522271)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Goršćak, Đurđica ; Leskovšek, Vojteh ; Godec, M. ; Vujnović, Srećko ; Kapuđija, D. ; Ćurković, Lidija
engleski
PERFORMANCE OF LOW-SILICON VACUUM REMELTED HOT WORK TOOL STEEL UNDER HIGH THERMAL LOAD
Exploitation of the critical parts in die casting moulds for radiators was observed for years and it was found that dominant wear mechanism was heat checking. After 1.2343 and 1.2367 grades, a vacuum remelted grade,  1.2343 with a lowered silicon content was used. At hardness of ca. 44 HRC, lifetime of the critical mould part significantly decreased, where heavy cracks occured. Notched impact energy and metallography of the mould part samples were analyzed.
aluminium alloy die casting mould; heat checking resistance; hot strength
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
191-198-x.
2006.
objavljeno
Podaci o matičnoj publikaciji
PROCEEDINGS OF 7TH INTERNATIONAL TOOLING CONFERENCE
MARIO, ROSSO, M. ACTIS, GRANDE, DANIEL, UGUES
Torino: POLITECNICO DI TORINO
Podaci o skupu
TOOLING MATERIALS AND THEIR APPLICATIONS FROM RESEARCH TO MARKET
predavanje
02.05.2006-05.05.2006
Torino, Italija