Low Carbon Steel Processed by Equal Channel Angular Warm Pressing


Zrnik, Jozef; Dobatkin, S. V.; Kraus, L.; Mamuzić, Ilija
Low Carbon Steel Processed by Equal Channel Angular Warm Pressing // Sažeci predavanja s 7. međunarodnog simpozija Hrvatskog metalurškog društva "Materijali i metalurgija", tiskano u Metalurgija 45(2006)3, 243-252 / Mamuzić, Ilija (ur.).
Zagreb: Hrvatsko metalurško društvo, 2006. str. 251-252 (poster, međunarodna recenzija, sažetak, znanstveni)


Naslov
Low Carbon Steel Processed by Equal Channel Angular Warm Pressing

Autori
Zrnik, Jozef ; Dobatkin, S. V. ; Kraus, L. ; Mamuzić, Ilija

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni

Izvornik
Sažeci predavanja s 7. međunarodnog simpozija Hrvatskog metalurškog društva "Materijali i metalurgija", tiskano u Metalurgija 45(2006)3, 243-252 / Mamuzić, Ilija - Zagreb : Hrvatsko metalurško društvo, 2006, 251-252

Skup
7. međunarodni simpozij Hrvatskog metalurškog društva "Materijali i metalurgija"

Mjesto i datum
Šibenik, Hrvatska, 18-22. 06. 2006

Vrsta sudjelovanja
Poster

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
Equal channel angular pressing (ECAP) ; low carbon steel ; increased temperatures

Sažetak
Commercial low carbon steel AISI 1010 was subjected to a severe plastic deformation technique called Equal Angular Channel Pressing (ECAP) at different increased temperatures. The paper describes the refinement of a course grained microstructure to submicrocrystalline structure by high strain plastic deformation. As temperature of ECAP straining is increasing the process of dynamic polygonization and recrystallization proceeds more effectively and subcrystalline structure is formed by sectioning of ferrite elongated grains. The size of newly born polygonized grains is in range of 300 - 500 μ m. The warm ECAP of the low carbon steel under specific testing condition leads to the formation of predominantly submicron grain structure. The formation of such of predominant submicrocrystalline structure resulted in significant increase of yield stress and tensile strength of the steel.

Izvorni jezik
Engleski

Znanstvena područja
Metalurgija



POVEZANOST RADA


Projekt / tema
0124001

Ustanove
Metalurški fakultet, Sisak

Autor s matičnim brojem:
Ilija Mamuzić, (27862)