Low-Cycle Strength and Cyclic Creep of a Molybdenum-Tungsten Alloy upon High-Temperature


Bukhanovskii, V. V.; Mamuzić, Ilija
Low-Cycle Strength and Cyclic Creep of a Molybdenum-Tungsten Alloy upon High-Temperature // Sažeci predavanja s 7. međunarodnog simpozija Hrvatskog metalurškog društva "Materijali i metalurgija", tiskano u Metalurgija 45(2006)3, 195-219
Zagreb: Hrvatsko metalurško društvo, 2006. str. 203-203 (poster, međunarodna recenzija, sažetak, znanstveni)


Naslov
Low-Cycle Strength and Cyclic Creep of a Molybdenum-Tungsten Alloy upon High-Temperature

Autori
Bukhanovskii, V. V. ; Mamuzić, Ilija

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, znanstveni

Izvornik
Sažeci predavanja s 7. međunarodnog simpozija Hrvatskog metalurškog društva "Materijali i metalurgija", tiskano u Metalurgija 45(2006)3, 195-219 / - Zagreb : Hrvatsko metalurško društvo, 2006, 203-203

Skup
7. međunarodni simpozij Hrvatskog metalurškog društva "Materijali i metalurgija"

Mjesto i datum
Šibenik, Hrvatska, 18-22. 06. 2006.

Vrsta sudjelovanja
Poster

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
Molybdenum-tungsten alloy ; low-cycle strength ; cyclic creep

Sažetak
The characteristics of low-cycle strength and cyclic creep of a Mo-30%W-NbC-C alloy produced by powder metallurgy are studied at temperatures of 1770, 2020, and 2270 K. In this temperature range the unified dependence of the cyclic steady-state creep rate on the ratio of the equivalent stress to the yield strength of the material at a certain temperature is obtained. Moreover, the generalized curve of the low-cycle strength of the alloy is constructed. The cyclic character of the loading accelerates the processes of directed plastic deformation and fracture in the powder alloy by a factor of 1, 5 -7 as compared to the corresponding long-term static loading, with the curves of cyclic and static creep being qualitatively similar.

Izvorni jezik
Engleski

Znanstvena područja
Metalurgija



POVEZANOST RADA


Projekt / tema
0124001

Ustanove
Metalurški fakultet, Sisak

Autor s matičnim brojem:
Ilija Mamuzić, (27862)