Eliashberg analysis of optical spectra reveals a strong coupling of charge carriers to spin fluctuations in doped iron-pnictide BaFe2As2 superconductors


Wu D.; Barišić, Neven; Dressel, M.; Cao, G.H.; Xu, Z.-A.; Schachinger, E.; Carbotte, J.P.
Eliashberg analysis of optical spectra reveals a strong coupling of charge carriers to spin fluctuations in doped iron-pnictide BaFe2As2 superconductors // Physical Review B - Condensed Matter and Materials Physics, 82 (2010), 144519-1 doi:10.1103/PhysRevB.82.144519 (međunarodna recenzija, članak, znanstveni)


Naslov
Eliashberg analysis of optical spectra reveals a strong coupling of charge carriers to spin fluctuations in doped iron-pnictide BaFe2As2 superconductors

Autori
Wu D. ; Barišić, Neven ; Dressel, M. ; Cao, G.H. ; Xu, Z.-A. ; Schachinger, E. ; Carbotte, J.P.

Izvornik
Physical Review B - Condensed Matter and Materials Physics (1098-0121) 82 (2010); 144519-1

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
PACS numbers: 74.25.Gz; 74.20.Mn; 74.20.Rp; 74.70.Xa

Sažetak
The temperature and frequency dependences of the optical conductivity of Co-doped BaFe2As2 are analyzed and the electron-boson spectral density 2F are extracted using Eliashberg’s formalism. For the normal state at T=30 K there is a relatively sharp and large peak around 10 meV and a secondary smaller and broader peak centered around 50 meV with the spectrum extending to high energies beyond the maximum phonon energy. The electron-boson mass enhancement parameter is 4.4, a value more consistent with spin-fluctuation scattering rather than with phonons. In addition the spectrum is found to evolve with temperature toward a less structured background at higher energies as in the spin susceptibility.

Izvorni jezik
Engleski

Znanstvena područja
Fizika



POVEZANOST RADA


Ustanove
Institut za fiziku, Zagreb

Autor s matičnim brojem:
Neven Barišić, (276012)

Časopis indeksira:


  • Current Contents Connect (CCC)
  • Web of Science Core Collection (WoSCC)
    • SCI-EXP, SSCI i/ili A&HCI
  • Scopus


Citati