Susceptibility to Hydrogen-Induced Cracking of Weld Beads on High-Strength Structural Steel


Malina, Jadranka; Samardžić, Ivan; Gliha, Vladimir
Susceptibility to Hydrogen-Induced Cracking of Weld Beads on High-Strength Structural Steel // Materials Science, 41 (2005), 2; 253-258 (međunarodna recenzija, članak, znanstveni)


Naslov
Susceptibility to Hydrogen-Induced Cracking of Weld Beads on High-Strength Structural Steel

Autori
Malina, Jadranka ; Samardžić, Ivan ; Gliha, Vladimir

Izvornik
Materials Science (1068-820X) 41 (2005), 2; 253-258

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Welding; hydrogen-induced cracking; TStE420

Sažetak
We study the hydrogen embrittlement and rupture of specimens of high-strength low-alloy steel with weld beads subjected to hydrogenation under the conditions of cathodic polarization. The specimens fail in the heat-affected zone on the boundary between the main metal and the weld bead in the zone of application of the latter and, especially, near its end. This explained by a higher hardness of the metal in this zone caused by the specific features of the temperature field formed in the process of welding.

Izvorni jezik
Engleski

Znanstvena područja
Metalurgija, Strojarstvo

Napomena
Published in Fizyko-Khimichna mekhanika materialiv, Vol 41, No. 2, pp. 101-104.



POVEZANOST RADA


Projekt / tema
0124006
0152011

Ustanove
Strojarski fakultet, Slavonski Brod

Časopis indeksira:


  • Web of Science Core Collection (WoSCC)
    • Science Citation Index Expanded (SCI-EXP)
    • SCI-EXP, SSCI i/ili A&HCI
  • Scopus