Characterization of oxide phases formed during the synthesis of Er3Fe5O12


Ristić, Mira; Czako-Nagy, Ilona; Popović, Stanko; Musić, Svetozar; Vertes, Attila; Ivanda, Mile
Characterization of oxide phases formed during the synthesis of Er3Fe5O12 // Journal of molecular structure, 410 (1997), 281-284 (međunarodna recenzija, članak, znanstveni)


Naslov
Characterization of oxide phases formed during the synthesis of Er3Fe5O12

Autori
Ristić, Mira ; Czako-Nagy, Ilona ; Popović, Stanko ; Musić, Svetozar ; Vertes, Attila ; Ivanda, Mile

Izvornik
Journal of molecular structure (0022-2860) 410 (1997); 281-284

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Er3Fe5O12. ErFeO3. X-ray diffraction. Mossbauer spectroscopy. Raman spectroscopy. Oxide phases

Sažetak
The mixed hydroxide 3Er(OH)(3) + 5Fe(OH)(3) was thermally treated up to 1300 degrees C. The samples obtained up to 650 degrees C were amorphous as observed by X-ray diffraction (XRD), The first appearance of Er_3Fe_5O_12 (ErIG) was observed in the sample obtained at 750 degrees C. The Fe-57 Mossbauer spectrum of the mixed hydroxide 3Er(OH)(3) + 5Fe(OH)(3) at room temperature was characterized by a quadrupole doublet (delta(Fe) = 0.38, Delta = 0.80, and Gamma = 0.50 mm s(-1)). After heating the starting material to 650 degrees C, the superposition of two quadrupole doublers and of a sextet of very small intensity with H = 506 kOe was observed. This result indicated that the amorphous fraction, detected by XRD, actually contained an additional Fe-bearing oxide phase of very fine particles which probably exhibited poor crystallinity, The sample obtained at 1300 degrees C was characterized by two hyperfine magnetic fields at room temperature with H-d = 394 and H-a = 489 kOe corresponding to ErIG, Selected samples were also characterized by laser Raman spectoscopy. (C) 1997 Elsevier Science B.V. [References: 5]

Izvorni jezik
Engleski

Znanstvena područja
Fizika, Kemija



POVEZANOST RADA


Projekt / tema
00980303
00980903

Ustanove
Institut "Ruđer Bošković", Zagreb

Časopis indeksira:


  • Current Contents Connect (CCC)
  • Web of Science Core Collection (WoSCC)
    • Science Citation Index Expanded (SCI-EXP)
    • SCI-EXP, SSCI i/ili A&HCI
  • Scopus