HREM, TEM and XRD observation of nanocrystalline phases in TiO2 obtained by the sol-gel method


Tonejc, Anđelka; Turković, Aleksandra; Gotić, Marijan; Musić, Svetozar; Vuković, Marijan; Trojko, Rudolf; Tonejc, Antun
HREM, TEM and XRD observation of nanocrystalline phases in TiO2 obtained by the sol-gel method // Materials letters, 31 (1997), 127-131 (međunarodna recenzija, članak, znanstveni)


Naslov
HREM, TEM and XRD observation of nanocrystalline phases in TiO2 obtained by the sol-gel method

Autori
Tonejc, Anđelka ; Turković, Aleksandra ; Gotić, Marijan ; Musić, Svetozar ; Vuković, Marijan ; Trojko, Rudolf ; Tonejc, Antun

Izvornik
Materials letters (0167-577X) 31 (1997); 127-131

Vrsta, podvrsta i kategorija rada
Radovi u časopisima, članak, znanstveni

Ključne riječi
Titanium dioxide; nano- material; sol-gel procedure
(Titanium dioxide; nano-material; sol-gel procedure)

Sažetak
The microstructural and chemical properties of nanosized TiO2 obtained by the sol-gel procedure, were investigated. The specific surface area of TiO2 was dependent on modifications of the general sol-gel procedure. A gradual decrease of the specific surface area (BET) from 169.9 to 2.7 m2/g with an increase of the calcination temperature up to 983 K was observed. At 913 K rutile was observed, together with a small amount of anatase. The grain size of the anatase phase changed from 4.5 mm to 6.5 mm when the temperature increased up to 913 K. The high specific surface area, small grain size, adequate porosity, and favorable phase composition of nanosized TiO2, synthesized in the present work, rendered this material suitable as photoelectrode in dye-senstized solar cells.

Izvorni jezik
Engleski

Znanstvena područja
Fizika, Kemija



POVEZANOST RADA


Ustanove
Institut "Ruđer Bošković", Zagreb,
Prirodoslovno-matematički fakultet, Zagreb

Časopis indeksira:


  • Current Contents Connect (CCC)
  • Web of Science Core Collection (WoSCC)
    • Science Citation Index Expanded (SCI-EXP)
    • SCI-EXP, SSCI i/ili A&HCI
  • Scopus