Fatigue life assessement of engine lateral supports


Domazet, Željko; Barle, Jani; Đukić, Predrag
Fatigue life assessement of engine lateral supports // 15th Symposium "Danubia-Adria" / Freddi, Alessandro (ur.).
Bologna: DIEM - Bologna, 1998. str. 105-106 (predavanje, međunarodna recenzija, sažetak, stručni)


CROSBI ID: 18372 Za ispravke kontaktirajte CROSBI podršku putem web obrasca

Naslov
Fatigue life assessement of engine lateral supports

Autori
Domazet, Željko ; Barle, Jani ; Đukić, Predrag

Vrsta, podvrsta i kategorija rada
Sažeci sa skupova, sažetak, stručni

Izvornik
15th Symposium "Danubia-Adria" / Freddi, Alessandro - Bologna : DIEM - Bologna, 1998, 105-106

Skup
15th Symposium "Danubia-Adria" on experimental methods in solid mechanics

Mjesto i datum
Bertinoro, Italija, 30.09.-03.10. 1998

Vrsta sudjelovanja
Predavanje

Vrsta recenzije
Međunarodna recenzija

Ključne riječi
Fatigue cracks; engine lateral support; hot-spot stresses

Sažetak
Fatigue failures of the main engine lateral supports (top engine bracing) of several bulk carrier vessels have been analyzed. Failures occurred after a few months of service. In order to solve the problem and avoid future time and money losses, it was necessary to establish main causes of failures. The strain gage measurements were performed in large scale during the sea trial. Possible reasons for these fatigue failures are: - loads are higher than one used for design of supports, - weldments are not correctly manufactured, - design of supports is inadequate. To obtain operational loads (axial force and the bending moments) strain gages were installed on each beam (1÷5 on Fig. 1.). The significant difference of measured axial forces between supports was discovered. One of the beams was loaded with approx. 50% lower load than the others. However, maximal axial force (20kN) was within a range of design load values. Measurements gave no significant bending moments. Stresses at the crack initiation points were measured to describe the quality of design. Strain gages 6÷8 were used for extrapolation of maximal stresses. Typical time record of measured local stresses is shown in Fig.2. The values of maximal stresses at the end of the weld are extrapolated, Fig. 3. According to [1], and to the determined maximal stresses it is possible to predict the fatigue life of approx. 5ˇ106 cycles, or a few weeks of service. This service life is too short, compared with expected 20 years. This prediction is in good agreement with the time to failure observed on former failures. Failures are mainly caused by inadequate design, of the joint of support and ship (hull) structure from one side, and insufficient weld quality.

Izvorni jezik
Engleski

Znanstvena područja
Strojarstvo



POVEZANOST RADA


Projekti:
023031
023033
023041

Ustanove:
Fakultet elektrotehnike, strojarstva i brodogradnje, Split

Profili:

Avatar Url Željko Domazet (autor)

Avatar Url Predrag Đukić (autor)


Citiraj ovu publikaciju:

Domazet, Željko; Barle, Jani; Đukić, Predrag
Fatigue life assessement of engine lateral supports // 15th Symposium "Danubia-Adria" / Freddi, Alessandro (ur.).
Bologna: DIEM - Bologna, 1998. str. 105-106 (predavanje, međunarodna recenzija, sažetak, stručni)
Domazet, Ž., Barle, J. & Đukić, P. (1998) Fatigue life assessement of engine lateral supports. U: Freddi, A. (ur.)15th Symposium "Danubia-Adria".
@article{article, author = {Domazet, \v{Z}eljko and Barle, Jani and \DJuki\'{c}, Predrag}, editor = {Freddi, A.}, year = {1998}, pages = {105-106}, keywords = {Fatigue cracks, engine lateral support, hot-spot stresses}, title = {Fatigue life assessement of engine lateral supports}, keyword = {Fatigue cracks, engine lateral support, hot-spot stresses}, publisher = {DIEM - Bologna}, publisherplace = {Bertinoro, Italija} }
@article{article, author = {Domazet, \v{Z}eljko and Barle, Jani and \DJuki\'{c}, Predrag}, editor = {Freddi, A.}, year = {1998}, pages = {105-106}, keywords = {Fatigue cracks, engine lateral support, hot-spot stresses}, title = {Fatigue life assessement of engine lateral supports}, keyword = {Fatigue cracks, engine lateral support, hot-spot stresses}, publisher = {DIEM - Bologna}, publisherplace = {Bertinoro, Italija} }




Contrast
Increase Font
Decrease Font
Dyslexic Font