Possible Improvements of Clinical Properties od Dental Composite Materials with Pulsed Blue Laser Curing

Despite considerable improvements of dental composite materials, the present-day composite resins still suffer from two major shortcomings that limit their use: inadequate degree of conversion and polymerization shrinkage. The objective of this study was to evaluate the degree of conversion and polymerization shrinkage of two hybrid and two microfilled composite materials cured by pulsed blue dye laser pumped XeCl excimer laser at 308 nm and the standard curing unit. The degree of conversion was measured by a Perkin Elmer FTIR spectrometer at the surface of the material and at a 3.0 mm depth. Statistical analysis showed a significantly higher degree of conversion values in the case of pulsed laser. Polymerization shrinkage measured by a pycnometer showed significantly lower values in the case of pulsed laser curing for six out of eight materials observed. The saturation effect in the material illuminated by monochromatic blue pulsed laser light may be responsible for the higher degree of conversion, while the relaxation of the molecules between nanopulses may lead to a reduced polymerization shrinkage.

blue laser curing; photopolymerization; polymerization shrinkage

nije evidentirano