High Temperature Strength of Niobium Alloy 5VMTs with a Silicide Ceramic Coating, Part1. Short Term Strength Characteristics (CROSBI ID 106750)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Bukhanovski, V. ; Borisenko, A. ; Kharchenko, K. ; Mamuzić, Ilija High Temperature Strength of Niobium Alloy 5VMTs with a Silicide Ceramic Coating, Part1. Short Term Strength Characteristics // Strength of materials, 36 (2004), 2; 119-129

Podaci o odgovornosti

Bukhanovski, V. ; Borisenko, A. ; Kharchenko, K. ; Mamuzić, Ilija

ruski

High Temperature Strength of Niobium Alloy 5VMTs with a Silicide Ceramic Coating, Part1. Short Term Strength Characteristics

Experimental dana on the short-term strength and plasticity of niobium alloy 5VMTs of the system Nb-W-Mo-Zr in its initial state, after annealing, and with a silicide-ceramic protective coating obtained by testing in vacuum, an inter atmosphere, and in air in the temperature range from 290 to 2270 K are analyzed. The process of microcrack initiation and propagation in the protective coating and matrix is investigated in high-temperature static tension. The limiting plastic strain values have been established at which the composite retains its load-carrying capacity in high-temperature aggressive and oxidizing gas atmospheres.

niobium alloy ; silicide-ceramic protective coating ; composite ; high temperatures load-carryng capacity

nije evidentirano

engleski

High Temperature Strength of Niobium Alloy 5VMTs with a Silicide Ceramic Coating, Part1. Short Term Strength Characteristics

nije evidentirano

niobium alloy ; silicide-ceramic protective coating ; composite ; high temperatures load-carryng capacity