Aluminum bronze BrA9Zh3L per GOST 493 solid state transformations and properties processing (CROSBI ID 730129)
Prilog sa skupa u časopisu | sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Uzlov, K. I. ; Repiakh, S. I. ; Dziubina, A. V. ; Mamuzić, Ilija
engleski
Aluminum bronze BrA9Zh3L per GOST 493 solid state transformations and properties processing
According to aluminum-ferrous bronze BrA9Zh3L microstructure and reticular characteristics studies results, it has been found that under significant undercooling (cooling rate> 1°C /min) below eutectoid temperature (at ~ 500 °C), martensitic transformation occurs with high-temperature β-phase stabilization and/or its martensitic derivatives: β1, β1´, β´, etc. formation. Technological or natural impurity Zn>0, 2…0, 3 % content leads to impact properties catastrophic decreasing. This is due to in alloy, as eutectoid structure α+γ2 component, rhombohedral chemical compound γ2-Cu9Al4 of trigonal system formation. That is, such Zn content stimulates in lowtemperature region (<565°) diffusion eutectoid transformation with γ2-phase with its reticular characteristics negative for material of product formation.
Aluminum bronze ; properties
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
315-315.
2023.
nije evidentirano
objavljeno
Podaci o matičnoj publikaciji
Metalurgija
Mamuzić, Ilija
Zagreb: Hrvatsko metalurško društvo
0543-5846
1334-2576
Podaci o skupu
16th International Symposium of Croatian Metallurgical Society - SHMD '2023, Materials and metallurgy
predavanje
20.04.2023-21.04.2023
Zagreb, Hrvatska
Povezanost rada
Metalurgija