Suppressing the Hofmeister Anion Effect by Thermal Annealing of Thin-Film Multilayers Made of Weak Polyelectrolytes (CROSBI ID 316468)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Klačić, Tin ; Bohinc, Klemen ; Kovačević, Davor Suppressing the Hofmeister Anion Effect by Thermal Annealing of Thin-Film Multilayers Made of Weak Polyelectrolytes // Macromolecules, 55 (2022), 9571-9582. doi: 10.1021/acs.macromol.2c01517

Podaci o odgovornosti

Klačić, Tin ; Bohinc, Klemen ; Kovačević, Davor

engleski

Suppressing the Hofmeister Anion Effect by Thermal Annealing of Thin-Film Multilayers Made of Weak Polyelectrolytes

Thin films made of weak polyelectrolytes poly(allylamine hydrochloride) (PAH) and poly(acrylic acid) (PAA) have been fabricated on silicon wafers using the layer-by-layer (LbL) method. To study the influence of counteranion type on the growth and properties of PAH/PAA multilayers, the nature of the supporting sodium salt was varied from cosmotropic to chaotropic anions (F–, Cl–, and ClO4–). Results of ellipsometry and AFM measurements indicate that the film thickness and surface roughness systematically increase on the order F– < Cl– < ClO4–. Furthermore, we found that the hydrophobicity of the PAH/PAA multilayer also follows the described trend when a polycation is the terminating layer. However, the heating of PAH/PAA multilayers to 60 °C during the LbL assembly suppressed the influence of background anions on the multilayer formation and properties. On the basis of the obtained results, it could be concluded that thermal annealing induces changes at the polymer–air interface in the sense of reorientation and migration of polymer chains.

polyelectrolyte multilayers ; ion-specific effect ; heating effect ; contact angle ; atomic force microscopy ; ellipsometry

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

55

2022.

9571-9582

objavljeno

0024-9297

1520-5835

10.1021/acs.macromol.2c01517

Povezanost rada

Kemija

Poveznice
Indeksiranost