Thermal stability and properties of Pd/CeAlO3 catalyst prepared by combustion synthesis (CROSBI ID 723827)
Prilog sa skupa u zborniku | sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Kurajica, Stanislav ; Mandić, Vilko ; Mužina, Katarina ; Panžić, Ivana ; Kralj, Damir ; Duplančić, Marina ; Ivković, Ivana Katarina
engleski
Thermal stability and properties of Pd/CeAlO3 catalyst prepared by combustion synthesis
Synthesis and characterization of cerium aluminate catalyst was investigated. The catalyst was prepared via combustion synthesis involving aluminum and cerium nitrates and glycine in the presence of palladium chloride. The obtained material was investigated using X-ray diffraction, Fourier transformed infra-red spectroscopy, differential thermal and thermo-gravimetric analysis, N2 adsorption, Raman spectroscopy, scanning electron microscopy and energy dispersion X-ray spectroscopy. Catalytic activity was tested for the toluene oxidation process. The direct product of combustion synthesis was CeAlO3 which remained stable even after thermal treatment at 400 °C for 2 h in static air, while temperature treatment at 800 °C for 2 h resulted in the decomposition of CeAlO3 into CeO2 and γ- Al2O3. Both thermal treatment products had sponge- like microstructure, but relatively small specific surface areas. Nevertheless, CeO2 prepared at 800 °C was nanocrystalline. Palladium was present as oxide homogeneously dispersed throughout the catalyst. The prepared catalyst proved to be highly active for the toluene oxidation process.
cerium aluminate ; palladium ; combustion synthesis ; catalysis
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
59-59.
2022.
objavljeno
Podaci o matičnoj publikaciji
Erceg, Matko ; Rotaru, Andrei ; Vrsalović, Ladislav
978-606-11-8164-3
Podaci o skupu
1th Central and Eastern European Conference on Physical Chemistry and Materials Science (CEEC-PCMS1)
predavanje
26.07.2022-30.07.2022
Split, Hrvatska