Corosion Fracture Mechanisms of Ziroconium Alloys in Iodine Containing Environment (CROSBI ID 716073)
Prilog sa skupa u časopisu | sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Nikulin, S. A. ; Khanzhin, V. G. ; Mamuzić, Ilija
engleski
Corosion Fracture Mechanisms of Ziroconium Alloys in Iodine Containing Environment
Tests of thin-walled tubes made of industrial zirconium alloys E110 and E635 (including a new modifications of these alloys) for stress corrosion cracking (SCS) in an aggressive corrosion environment of iodine-methanol have been carried out. Time to failure of alloys is determined and corrosion damageability is assessed. Corrosion fracture mechanisms observed in zirconium alloys are analyzed on micro and macro levels.
Ziroconium alloys ; Iodine ; corosion fracture mechanisms
Konferencija je otkazana zbog pandemije COVID-19, ali su svi konferencijski materijali objavljeni.
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
890-890.
2022.
nije evidentirano
objavljeno
Podaci o matičnoj publikaciji
Metalurgija
Mamuzić, Ilija
Zagreb: Hrvatsko metalurško društvo
0543-5846
1334-2576
Podaci o skupu
15th International Symposium of Croatian Metallurgical Society (SHMD '22)
poster
22.03.2022-23.03.2022
Zagreb, Hrvatska
Povezanost rada
Metalurgija