CHARACTERIZATION OF pH SENSOR FILMS PREPARED BY THE SOL-GEL METHOD (CROSBI ID 715773)
Prilog sa skupa u zborniku | sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Drmić, Katarina Marija ; Geršak, Inga ; Marković, Marijan-Pere ; Vrsaljko, Domagoj
engleski
CHARACTERIZATION OF pH SENSOR FILMS PREPARED BY THE SOL-GEL METHOD
The aim of this work is to determine the working range of the pH indicator after immobilization, to characterize the functional groups using Fourier-transform infrared spectroscopy (FTIR), and to determine whether the hydrophilicity of the surface changes when the coating is applied. In addition, the effect of post-curing and swelling of polyacrylate test plates in various solvents on coating adhesion was investigated. The degree of cure (DOC) of the plates was determined using DSC method. The test plates were manufactured using stereolithography (SLA) 3D-printing technology (Clear material) and sol-gel method was used to prepare the pH sensor films. The mixture for sensor film coating was prepared using silane precursors tetraethoxysilane (TEOS) and phenyltrimethoxysilane (FTMS), ethanol/water as solvent and hydrochloric acid (HCl) as catalyst for the sol-gel process with the addition of pH indicators. The indicators used in this work were methyl red and litmus. The functionality of the sensor film was investigated by placing the test plates covered with pH sensor films in ten solutions with different pH values. After the test, it can be seen that the pH sensor films change color depending on the pH of the solution (Fig. 1).
Additive manufacturing ; sensor film ; sol-gel
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
100-100.
2022.
objavljeno
Podaci o matičnoj publikaciji
XIV. SUSRET MLADIH KEMIJSKIH INŽENJERA KNJIGA SAŽETAKA
Podaci o skupu
XIV. susret mladih kemijskih inženjera (SMLKI 2022)
poster
24.02.2022-25.02.2022
Zagreb, Hrvatska