The influence of Nb content on the crystal latice distortion of a final thermomechanical treatment microalloyed steel (CROSBI ID 711817)

Prilog sa skupa u časopisu | sažetak izlaganja sa skupa | međunarodna recenzija

Vodopivec, F. ; Rešković, S. ; Mamuzić, Ilija The influence of Nb content on the crystal latice distortion of a final thermomechanical treatment microalloyed steel // Metalurgija / Mamuzić, Ilija (ur.). 2022. str. 553-554

Podaci o odgovornosti

Vodopivec, F. ; Rešković, S. ; Mamuzić, Ilija

engleski

The influence of Nb content on the crystal latice distortion of a final thermomechanical treatment microalloyed steel

Studies have been performed on microalloyed steel with three different niobium content: 0, 036%, 0, 048% and 0, 066%. All steels had the same basic chemical composition. Samples for research were taken from different phases of final thermomechanical treatment. The samples were analyzed by transmission electron analysis and X-ray diffraction profile analysis. Precipitation of niobium carbonitrides was observed in all tested samples. In steels with 0, 048% nobium, densely complex carbonitride arrays were observed in the grain and along the boundaries of the crystal grain. The highest degree of interaction between deformation of induced nobium precipitates and dislocations was found in steels with o, o48% Nb. The largest distortion of the crystal lattice was determined on the same samples. In steel with 0, 036% niobium is less pronounced and the crystal lattice distortion is less.

microalloyed steel ; niobium content ; thermomechanical treatment

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o prilogu

553-554.

2022.

nije evidentirano

objavljeno

Podaci o matičnoj publikaciji

Metalurgija

Mamuzić, Ilija

Zagreb: Hrvatsko metalurško društvo

0543-5846

1334-2576

Podaci o skupu

15th International Symposium of Croatian Metallurgical Society (SHMD '22)

poster

22.03.2022-23.03.2022

Zagreb, Hrvatska

Povezanost rada

Metalurgija

Poveznice
Indeksiranost