The effect of modification with silicon carbide on the mechanical properties of the secondary aluminum alloy of the Al-Si system (CROSBI ID 711659)
Prilog sa skupa u časopisu | sažetak izlaganja sa skupa | međunarodna recenzija
Podaci o odgovornosti
Selivorstov, V. ; Dotsenko, Yu. ; Nasonov, D. ; Mamuzić, Ilija
engleski
The effect of modification with silicon carbide on the mechanical properties of the secondary aluminum alloy of the Al-Si system
The effect of modification on the mechanical properties of the secondary aluminum casting alloy (wt.%: 0, 528 Mg, 1, 124 Cu, 11, 539 Si, 84, 969 Al, 0, 905 Fe, 0, 692 Zn, 0, 242 Mn) without heat treatment was determined by the introduction of silicon carbide with a particle size of 1-3 μm in the amount of 0, 1, 0, 2, 0, 3 wt. %. When the content of SiC in the alloy from 0, 1 % to 0, 2%, the indicators of Rm increase from 130-145 MPa to 155-166 MPa, respectively. Increasing the SiC content to 0, 3% leads to a decrease in Rn values in the range of 117 - 127 MPa. Hardness indices (HD): unmodified alloy - 42 - 43, alloy with a content of 0, 1% SiC - 43 - 44, with a content of 0, 2% SiC - 46 - 47, with a content of 0, 3% SiC - 43 – 44.
secondary aluminum casting alloy ; mechanical properties ; silicon carbide
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
553-553.
2022.
nije evidentirano
objavljeno
Podaci o matičnoj publikaciji
Metalurgija
Mamuzić, Ilija
Zagreb: Hrvatsko metalurško društvo
0543-5846
1334-2576
Podaci o skupu
15th International Symposium of Croatian Metallurgical Society (SHMD '22)
poster
22.03.2022-23.03.2022
Zagreb, Hrvatska
Povezanost rada
Metalurgija