Corrosion study of CuAlNi alloy in stirred H2SO4 solution (CROSBI ID 704505)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Vrsalović, Ladislav ; Gudić, Senka ; Šućurović, Verena ; Ivanić, Ivana ; Kožuh, Stjepan ; Gojić, Mirko ; Kosec, Borut
engleski
Corrosion study of CuAlNi alloy in stirred H2SO4 solution
CuAlNi alloy has been evaluated for its corrosion behaviour in the 0.5 mol dm-3 H2SO4 stirred solution at the rotation rate of magnetic stirrer of 150 and 450 rpm, at 20 and 40 oC. Investigations were performed using open circuit potential measurements, linear and polarization measurements. After polarization measurements corroded surfaces were evaluated using light microscopy analysis. It was found that increasing in electrolyte temperature leads to higher corrosion damages of alloy while increase in rotation rate of stirrer has smaller impact on corrosion. The presence of intergranular corrosion on the electrode surfaces was clearly seen with optical microscope.
CuAlNi alloy, corrosion, polarization, optical microscopy
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
482-488.
2021.
objavljeno
Podaci o matičnoj publikaciji
Proceedings Book 19th International Foundryman Conference, Humans-Valuable Resource for Foundry Industry Development
Dolić, Natalija ; Brodarac, Zdenka Zovko ; Brajčinović, Sandra
Sisak: Metalurški fakultet Sveučilišta u Zagrebu
978-953-7082-38-3
Podaci o skupu
19th International Foundrymen Conference Humans – Valuable Resource for Foundry Industry Development
poster
16.06.2021-18.06.2021
Split, Hrvatska