Mechanochemical pretreatment of ammonia borane: A new procedure for sodium amidoborane synthesis (CROSBI ID 266609)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Milanović, Igor ; Biliškov, Nikola
engleski
Mechanochemical pretreatment of ammonia borane: A new procedure for sodium amidoborane synthesis
The present work reports a new procedure for solid state synthesis of sodium amidoborane (NaAB) by mechanochemical (MC) reaction between as-received NaH and MC pretreated AB. Ball milling (BM) method was used for this purpose. Firstly, pretreated AB was obtained by BM of as-received AB for 4.5 min. Secondly, powder of pretreated AB was mixed with as-received NaH and conducted to BM. Milling times were from 0 to 200 min: 5, 10, 30, 50, 100 and 200 min, respectively. By fixing the parameters of the milling conditions, only the influence of milling time on NaAB formation was followed. FTIR and XRD methods are used for analysis of powders after milling. We proved, by MC modification of pure AB, that the reaction rate between AB and NaH could be restricted to the interface between newly formed larger AB and small NaH particles. On such a way we obtained much better control of the reaction system with very accurate determination of reaction steps. Depending on the milling times, reaction process can be separated in three parts: i) 0–30 min part - reactant and product are present ; ii) 50–100 min part - formed NaAB is almost without other phases ; iii) 200 min part - NaAB is totally decomposed. By that synthesis procedure we produced, for the first time, pure NaAB almost without any impurity.
Ammonia borane ; amidoboranes ; ball milling ; mechanochemistry ; XRD ; IR spectroscopy ; Hydrides ; hydrogen storage
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
45 (14)
2020.
7938-7946
objavljeno
0360-3199
1879-3487
10.1016/j.ijhydene.2019.06.042