Effect of subsequent heating on the microstructure and mechanical properties of Nb microalloyed steel (CROSBI ID 676556)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Slokar Benić, Ljerka ; Jandrlić, Ivan ; Rešković, Stoja
engleski
Effect of subsequent heating on the microstructure and mechanical properties of Nb microalloyed steel
Effect of subsequent heating on the microstructure and mechanical properties of hot rolled niobium microalloyed steel was researched in this paper. Low carbon steel was microalloyed with 0.048 % niobium and it was heated at 1150C followed by cooling in the air. Researches were performed on two types of samples: low carbon steel microalloyed with niobium and subsequently heated microalloyed steel in the rolling direction as well as in the direction perpendicular to the rolling direction. Mechanical properties of all samples were determined by the static tensile test at testing rate of 5 mm/min. After that their microstructure was observed by scanning electron microscope. Results have shown a significant effect of subsequent heating on the microstructure, i.e. grain size as well as on the mechanical properties.
subsequent heating, niobium microalloyed steel, microstructure, mechanical properties
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
180-187.
2019.
objavljeno
Podaci o matičnoj publikaciji
18th International foundrymen conference, Coexistence of material science and sustainable technology in economic growth
Dolić, Natalija ; Zovko Brodarac, Zdenka ; Begić Hadžipašić, Anita
Sisak: Metalurški fakultet Sveučilišta u Zagrebu
978-953-7082-34-5
Podaci o skupu
18. Međunarodno savjetovanje ljevača "Suživot znanosti o materijalima i održive tehnologije u gospodarskom rastu" = 18th International Foundryman Conference "Coexistence of material science and sustainable technology in economic growth"
predavanje
15.05.2019-17.05.2019
Sisak, Hrvatska